Method of manufacturing a trench MOSFET using selective growth epitaxy

ABSTRACT

A method of manufacturing a trench structure for a trench MOSFET, including the steps of providing a semiconductor substrate having a major surface, forming a dielectric pillar on the substrate major surface (the dielectric pillar extending substantially perpendicularly from the major surface of the substrate), selectively forming a semiconductor layer around the dielectric pillar, and removing a predetermined length of the dielectric pillar to create a trench in the substrate, the trench defined by sidewalls and a bottom. The method permits the controlled formation of a dielectric plug at the bottom of the trench, the plug having predetermined dimensions.

CROSS-REFERENCE TO RELATED APPLICATIONS

This is a continuation-in-part of U.S. patent application Ser. No. 09/586,720, filed on Jun. 5, 2000, now U.S. Pat. No. 6,391,699.

BACKGROUND OF THE INVENTION

The present invention relates in general to semiconductor technology, and in particular, to a method of manufacturing a trench doubly-diffused Metal Oxide Semiconductor Field Effect transistor (trench DMOS transistor) using selective growth epitaxy.

A cross-sectional view of a typical n-channel trench DMOS transistor 10 is shown in FIG. 1. It includes an n-type substrate 100 upon which an n-type epitaxial layer 102 is typically grown. A p-type body layer 108 covers epitaxial layer 102 and one or more trenches 100 extend through the body layer 108 and a portion of the epitaxial layer 102. Gate oxide layer 104 line the sidewalls and bottom of each trench 100 and a conductive material 106, typically doped polysilicon, lines gate oxide layer 104 and fills each trench 100. N+ source regions 110 flank each trench 100 and extend a predetermined distance into body layer 108. Heavy body regions 112 are positioned within body layer 108 and between source regions 110 and extend a predetermined distance into body layer 108. Finally, dielectric caps 114 cover the filled trenches 100 and also partially cover the source regions 110.

During fabrication of the trench DMOS transistor 10, an anisotropic etch step is typically performed to form trenches 100. An anisotropic etch is used, as opposed to an isotropic etch, since an anisotropic etch etches substantially in one direction, which in this example, is vertical and downward. A drawback of administering an anisotropic etch is that the sidewalls become damaged, i.e. silicon surface defects are created. This leads to a degraded gate oxide 104 to trench sidewall interface and a concomitant degradation in the quality of the gate oxide 104 itself.

After trenches 100 are formed, a dielectric layer such as silicon dioxide (or oxide) is typically grown over the bottom and sidewalls of the trench to form a gate oxide. Simultaneous formation of the oxide at the bottom and on the sidewalls of the trenches limits the thickness of the oxide that can be grown on the bottom of the trenches 100, since growth on the sidewalls eventually pinches off growth on the bottom of the trenches 100. A thin oxide on the bottom of the trench is undesirable since it leads to a lower breakdown voltage of the device and an undesirably large gate-to-drain capacitance.

Limiting oxide growth on the trench sidewalls while growing oxide on the bottom of the trench can be accomplished by using a masking technique such as LOCOS (Local Oxidation of Silicon). Unfortunately, this sidewall masking technique creates problems such as oxide stress near the comers of a trench and formation of a “bird's head” at the upper and lower comers of the trench. These bird's heads are undesirable. For example, the presence of bird's heads at the upper trench comers leads to step-coverage problems of overlying metal layers, due to the uneven surface topology caused by the bird's heads. While an etchback of the LOCOS layer can somewhat reduce the presence of the bird's head, there still remains the problem of reliably growing an oxide layer on the bottom of the trench to a predetermined thickness.

SUMMARY OF THE INVENTION

In a first aspect of the invention, a method of forming a trench in a semiconductor substrate is disclosed. The method comprises the steps of: providing a semiconductor substrate; forming a pillar of dielectric material on the substrate, the pillar having a top surface and a predetermined thickness; forming a semiconductor layer over the substrate and around and over the top surface of the pillar; forming a masking layer over the semiconductor layer, the masking layer having a trench opening access that exposes a portion of an upper surface of the semiconductor layer and being in substantial vertical alignment with the pillar; and forming a trench through the trench opening access by anisotropically etching the semiconductor layer down to the top surface of the pillar. Preferably, the dielectric pillar is silicon dioxide and is formed via thermal oxidation.

In a second aspect of the invention, a method of manufacturing a trench MOSFET is disclosed. The method comprises the steps of: providing a semiconductor substrate having a first conductivity type; forming a first semiconductor layer over the substrate, the first semiconductor layer having the first conductivity type; forming a plurality of dielectric pillars across a surface of the first semiconductor layer, each pillar having a top surface and predetermined height; forming a second semiconductor layer having the first conductivity type over the first semiconductor layer and around and over the top surfaces of the pillars; forming a third semiconductor layer over the second semiconductor layer, the third semiconductor layer having a second conductivity type; forming a masking layer over the third semiconductor layer, the masking layer defining a plurality of trench opening accesses that expose portions of an upper surface of the third semiconductor layer and being in substantial vertical alignment with the pillars; forming a plurality of trenches through the trench opening accesses by anisotropically etching the third semiconductor layer and a portion of the second semiconductor layer and down to the top surfaces of the pillars; removing the masking layer; lining sidewalls of the trenches with a dielectric material; and lining the dielectric material and filling the trenches with a conductive material.

In an alternative embodiment to the second aspect of the invention source and heavy body regions are formed by standard implant and drive techniques and a dielectric cap is then formed over openings to the trenches and over a portion of the source regions.

In a third aspect of the invention a trench structure is disclosed, the trench structure comprising: A trench structure, comprising: a semiconductor substrate; a first semiconductor layer formed over the substrate; a second semiconductor layer selectively formed over the first semiconductor layer; a trench extending from an exposed primary surface of the second semiconductor layer and through the first and second semiconductor layers; and a dielectric column positioned at the bottom of the trench, the column having a substantially flat upper surface and a precisely controlled and predetermined thickness. Preferably the dielectric column is formed by thermal oxidation.

In a fourth aspect of the invention a trench MOSFET is disclosed, the trench MOSFET, comprising: a substrate having a first conductivity type; a first semiconductor layer having the first conductivity type formed over the substrate; a second semiconductor layer having the first conductivity type selectively formed over the first semiconductor layer; a third semiconductor layer having a second conductivity type selectively formed over the second semiconductor layer; a plurality of trenches extending from an exposed primary surface of the third semiconductor layer and through the third and second semiconductor layers, each trench defined by a bottom and walls; a dielectric column positioned at the bottom of each trench, the column having a substantially flat upper surface and a precisely controlled and predetermined thickness; a dielectric material lining the walls of the trenches; and a conductive material lining the dielectric material and filling the trenches.

In a fifth aspect of the invention dielectric caps are formed over openings of the trenches in the trench MOSFET described in the previous paragraph. These caps isolate the source regions from the gate region of the trench MOSFET. Each cap has lateral dimensions that are substantially equal to the lateral dimensions of the trenches. These dimensions allow a lower trench-to-trench pitch than what can be realized in prior art trench MOSFETs.

In a sixth aspect of the invention, a method of forming a trench structure is disclosed. The method comprises the steps of providing a semiconductor substrate having a major surface; forming a dielectric pillar on the substrate major surface, the dielectric pillar extending substantially perpendicularly from the major surface; selectively forming a semiconductor layer around the dielectric pillar; and removing a predetermined length of the dielectric pillar to create a trench in the substrate, the trench defined by sidewalls and a bottom. In this aspect of the invention a dielectric plug, having a predetermined thickness can be left at the bottom of the trench following the step of removing a predetermined length of the dielectric pillar.

In a seventh aspect of the invention, a method of manufacturing a trench field effect transistor is disclosed. The method comprises the steps of providing a semiconductor substrate having a major surface and a first conductivity type; forming a plurality of dielectric columns extending perpendicularly from the major surface of the substrate; selectively forming a first semiconductor layer having the first conductivity type over exposed areas of the major surface of the substrate and around the dielectric columns; selectively forming a second semiconductor layer having a second conductivity type, opposite to that of the first conductivity type, over the first semiconductor layer and around the dielectric columns; selectively forming a third semiconductor layer having the first conductivity type over the second semiconductor layer and around the semiconductor columns; removing a predetermined portion of each dielectric column to create a plurality of trenches extending through the third, second and a portion of the first semiconductor layer, each trench defined by a bottom and sidewalls; and lining the sidewalls of the trenches with a gate oxide.

A further understanding of the nature and advantages of the inventions herein may be realized by reference to the remaining portions of the specification and the attached drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional view of a typical trench MOSFET;

FIG. 2 is a process flow diagram showing exemplary process steps for manufacturing a trench according to a method of the present invention;

FIGS. 3A-3H are cross-sectional illustrations of the structure formed at various points in the process of FIG. 2;

FIG. 4 is a process flow diagram showing exemplary process steps for manufacturing a trench MOSFET according to a method of the present invention;

FIGS. 5A-5K are cross-sectional illustrations of the trench MOSFET structure formed at various points in the process of FIG. 4;

FIGS. 6A-6C are cross-sectional illustrations of a trench MOSFET showing the formation of source, heavy body and dielectric caps using an alternative embodiment of the method producing the structures shown in FIGS. 5I-5K;

FIG. 7 is a process flow diagram showing exemplary process steps for manufacturing at trench structure according to a method of the present invention;

FIGS. 8A-8D are cross-sectional illustrations of a trench structure formed at various points in the process shown in FIG. 7;

FIG. 9 is a process flow diagram showing exemplary process steps for manufacturing a trench MOSFET and incorporating the process shown in FIG. 7;

FIGS. 10A-10N are cross-sectional illustrations of a trench MOSFET formed at various points in the process shown in FIG. 9;

FIG. 11 is a process flow diagram showing exemplary process steps for manufacturing a trench MOSFET and incorporating the process shown in FIG. 7; and

FIGS. 12A-12J are cross-sectional illustrations of a trench MOSFET formed at various points in the process shown in FIG. 11.

DESCRIPTION OF THE SPECIFIC EMBODIMENTS

In a first embodiment of the present invention a novel method of creating a thermally grown dielectric such as silicon dioxide (or oxide) of any thickness at the bottom of a silicon trench is disclosed. Unlike prior art attempts, the oxide is grown prior to formation of the trench. Pillars of oxide are formed on the surface of the substrate. A selective epitaxial growth (SEG) process is used to form an epitaxial layer around the oxide pillars. Trenches are then patterned and etched in alignment with the pillars such that the trenches terminate on the top of the oxide pillars. This method is described in greater detail below.

Referring to FIG. 2, there is shown a flow diagram illustrating an exemplary process flow for manufacturing a trench having a thermally grown gate oxide of precisely controlled dimensions. The following description of the process flow is only exemplary and one skilled in the art would understand that the scope of the invention is not limited to this specific example. In particular, while the trench in this example is formed in an n-type substrate, it should be understood that the doping type of the substrate and other layers is merely exemplary and not limiting. Additionally, processing conditions such as temperature, pressure, layer thicknesses, etc., could vary without departing from the spirit of the invention. A detailed description of the process flow in FIG. 2 is now described in connection with FIGS. 3A through 3H.

The first step in the process, step 200, is to provide a substrate 300, as shown in FIG. 3A, the substrate having a standard thickness of, for example, 700 μm and resistivity of, for example, 5 mΩ-cm. In step 202, a first epitaxial layer 302 is grown over the substrate, as shown in FIG. 3B. At step 204, an oxide layer 304 is formed, preferably by a process of thermal oxidation, from the exposed surface of the first epitaxial layer 302. A cross-section of the structure formed at this juncture in the process is shown in FIG. 3C.

After oxide layer 304 has been formed, in step 206, oxide layer 304 is patterned and then etched by, for example, use of a photolithographic process, as is known in the art, to form oxide pillars 306 as shown in FIG. 3D.

Next, in step 208, a short sacrificial oxidation, having a thickness in this example about 0.03 μm is formed over the exposed areas of the first epitaxial layer 302. Then the sacrificial oxide is wet etched back to the epitaxial layer surface and the resulting structure is annealed in a hydrogen ambient to prepare the exposed epitaxial layer for formation of a second epitaxial layer. This step, 208, is optional and is not needed if the etched surface has no residual oxide or etch defects.

At step 210, a first portion 308 of a second epitaxial layer is formed. Preferably, formation of the first portion 308 is done using a process known as selective epitaxial growth (SEG). SEG is achieved upon a single crystal material, such as silicon, by providing a silicon source with halide atoms in it (e.g. Si source with HCl). The halide atoms enhance the surface mobility of the silicon atoms in the silicon source so that they are more able to migrate to sites on the material where nucleation is favored. The first portion 308 of the second epitaxial layer is grown to the point of coalescence, i.e., to the point where the silicon growing on both sides of the oxide pillars 306 meet after growing above the top of the oxide pillars 306. The structure at this point in the fabrication process is shown in FIG. 3E.

After coalescence is achieved, the halide source, in this example HCl gas, is turned off and in step 212, a second portion 310 of the second epitaxial layer is grown using a standard epitaxial growth technique. The structure at this point in the fabrication process is shown in FIG. 3F.

Next, at step 214 a hard mask 312 comprised of, for example, a nitride layer, preferably padded by an underlying pad oxide layer, is formed over the exposed surface of the second portion 310 of the second epitaxial layer and then patterned and selectively etched to form trench opening accesses 314, which are aligned with the oxide pillars 306 embedded below in the structure.

Next, at step 216, an anisotropic etch is performed through the trench opening accesses 314 to create trenches 316. Typically, the anisotropic etch is in the form of a plasma, which is an almost neutral mixture of energetic molecules, ions and electrons that have been excited in a radio-frequency electric field. Different gases are used depending on the material to be etched. The principal consideration is that the reaction products must be volatile. For etching silicon dioxide, the reactants may be, for example, Ar, CF₄, and CHF₃ the pressure may be, for example, 800 mT and the duration of the etch may be approximately 150 seconds. The structure following step 216 is shown in FIG. 3H.

A second aspect of the invention relates to using the method of forming a trench described above in the process of fabricating a trench DMOS transistor. A process flow diagram showing the steps of an exemplary method of fabricating a trench DMOS transistor according to the present invention is shown in FIG. 4. The following description of the process flow is only exemplary and it should be understood that the scope of the invention is not limited to this specific example. In particular, while the trench DMOS transistor described in this example is an n-channel device, a p-channel device could also be made by simply changing dopant types of the various layers. Additionally, processing conditions such as temperature, pressure, layer thicknesses, etc. could be possibly varied, without departing from the spirit of the invention. A detailed description of the process flow in FIG. 4 is now described in connection with FIGS. 5A through 5K.

The first step in the process, step 400, is to provide a substrate 500 having a standard substrate thickness (700 μm) and resistivity as shown in FIG. 5A. In step 502, a first portion 502 of the drain region for the trench DMOS transistor is grown over substrate 500. The structure following step 502 is shown in FIG. 5B.

In step 404 a thermal oxide layer 504 is grown from the first portion 502 of the drain region as shown in FIG. 5C. Then, in step 406 oxide layer is patterned and etched using standard photolithography to form oxide pillars 506 as is shown in FIG. 5D.

Next, in step 408, a sacrificial oxidation (0.03 μm) and wet etch is performed, followed by a hydrogen anneal to prepare the exposed surface of the first portion 502 of the drain region for selective epitaxial growth (SEG).

In step 410, the remaining portion 508 of the drain region is grown using SEG. The remaining portion 508 of the drain region is grown over the tops of oxide pillars 506 to the point of coalescence. The structure following this step in the process is shown in FIG. 5E.

After the desired drain thickness is obtained, a body region 510 is grown over the top surface of the remaining portion 508 of the drain region to a thickness of about 0.6 μm. This step 412 and the preceding step 410 could be performed in situ. This is accomplished by terminating the SEG process once the desired drain thickness is obtained and switching to non-selective epitaxial growth and a different doping source (e.g. boron) to form the body region 510 in step 412. The structure following step 412 is shown in FIG. 5F.

In step 414, a hard mask is formed over the body region 510. Preferably the hard mask is comprised of a nitride layer and an underlying pad oxide layer. Once formed over the body region 510, the hard mask is patterned and etched using standard photolithography to reveal trench opening accesses 514. As shown in FIG. 5G, the trench opening accesses 514 are in vertical alignment with the buried oxide pillars 506.

Next, in step 416, an anisotropic etch is performed through trench opening accesses 514 to form trenches 516 that terminate at the top of the oxide pillars 506. The structure following the anisotropic etch is shown in FIG. 5H.

In step 418, a sacrificial oxidation (0.02 μm) and wet etch is performed, followed by a hydrogen anneal (˜3 min. @ 1060° C.) and an argon anneal (˜20 min. @ 1100° C.) to repair etch damage, round upper and bottom comers of the trenches 516 and prepare trench sidewalls for gate oxidation.

In step 420, a gate oxide 518 is formed over the sidewalls of the trenches 516 to a thickness of about 0.4 μm and in step 422 the trenches 516 are filled with doped polysilicon 520.

In step 424, dielectric isolation regions 522 are formed over the polysilicon-filled trenches 516. These dielectric isolation regions 522 will function to isolate the gate from the source once the source is formed. The structure following step 424 is shown in FIG. 5I.

After the dielectric isolation regions 522 are formed, in step 426 an optional sacrificial oxidation (0.02 μm) and wet etch are both performed, followed by an optional hydrogen anneal (˜1 min. @ 1060° C.) to prepare the exposed surface of body layer 510 for growth of a source region.

In step 428, a source region 524 is grown using SEG to a thickness that just meets the tops of the dielectric isolation regions 522, thereby forming a substantially planar surface. If a higher dopant concentration than what can be achieved with SEG in situ doping is needed, a standard implantation process could be used to increase the dopant concentration. The structure following step 428 is shown in FIG. 5J. An alternative to the SEG technique used in step 428 is to use a non-selective epitaxial deposition approach to form the source region. This source region would then be patterned and etched using standard photolithography, after which oxide would be deposited in the etched areas to form the dielectric isolation regions.

Next, in step 430 a heavy body region 526 is formed using standard photolithography and implant and drive techniques. Finally, in step 432 a metal layer (˜5 μm) is deposited over the substantially planar surface.

In an alternative embodiment, steps 428 through 432 can be replaced with the following steps 428′ through 432′. In step 428′ the body region 510′ is further grown to a thickness that will allow the source and heavy body to be implanted in subsequent processing steps. The structure after performing step 428′ is shown in FIG. 6A.

In step 430′, source region 524′ and heavy body region 526′ are formed using standard patterning, implanting and driving. The structure following step 430′ is shown in FIG. 6B.

Finally, in step 432′ a dielectric layer is deposited, masked, etched and flowed to create a dielectric isolation region 522′ between the source and gate and a metal layer is deposited over the structure as shown in FIG. 6C.

Comparing FIG. 5K to FIG. 6C it is seen that dielectric isolation region 522′ is positioned over the source region 524′ in the embodiment shown in FIG. 6C, whereas the dielectric isolation region 522 is positioned within the source region 524 for the embodiment shown in FIG. 5K. This difference provides the embodiment shown in FIG. 5K with at least two advantages over the embodiment shown in FIG. 6C. First, because the dielectric isolation regions 522 are within the source region layer 524 and are not spaced laterally over it, a reduction in trench pitch can be realized to a larger degree than can be realized for the embodiment shown in FIG. 6C. Second, since the dielectric isolation region 522 is planar to the source region 524, better metal step coverage can be realized than can be for the embodiment shown in FIG. 6C.

In another embodiment of the present invention, a novel method of forming a dielectric such as, for example, silicon dioxide (or oxide) of any thickness at the bottom of a semiconductor trench is disclosed. An exemplary process flow diagram and cross-sections of the structure formed at various stages of the applied method are shown in FIG. 7 and FIG. 8, respectively. The first step in the process (step 700 in FIG. 7) is to provide a semiconductor substrate 800. Semiconductor substrate 800 may have a thickness of, for example, 700 μm and a resistivity of 5 mΩ-cm (for an N+ doping for example). Next, at step 702, a first n-type epitaxial layer 802 is grown over substrate 800. From this first epitaxial layer 802, a thermal oxide layer 804 is formed at step 704. A cross-section of the structure formed, following completion of step 704, is shown in FIG. 8A.

After oxide layer 804 is formed, in step 706 oxide layer 804 is patterned using, for example, a photolithographic process as is known in the art, and etched, preferably anisotropically, to create oxide pillars 806. A cross-section of the structure, following completion of step 706, is shown in FIG. 8B. Next, at optional step 708, a short sacrificial oxidation, having a thickness of, for example, 0.03 μm, is formed over the exposed areas of epitaxial layer 802. Then, the sacrificial oxide is wet etched back to the epitaxial layer surface and the resulting structure is annealed in hydrogen to prepare the surface for the next step.

At step 710, a selective epitaxial growth (SEG) process is used to form a second epitaxial layer 808 that surrounds oxide pillars 806. Second epitaxial layer 808 is grown to the point of coalescence, i.e., to the point where the silicon growing on both sides of oxide pillars 306 meet after growing above the top of the oxide pillars 806. The structure following step 710 is shown in FIG. 8C.

At step 712, an oxide-biased etch (preferably anisotropic) is performed to create trenches 810, which have a depth determined by the amount of oxide left in the bottom of the trenches. And, finally, at step 714 a sacrificial oxide wet etch and hydrogen anneal are performed.

The above method can be used to manufacture a trench DMOS transistor that has a well-controlled oxide thickness at the bottom of the trenches, which can be tailored to achieve a specified gate-to-drain capacitance. An exemplary process flow diagram, which includes the above method, and cross-sectional views of the structure formed at various stages in the process of manufacturing a trench DMOS transistor using the method are shown in FIGS. 9 and 10, respectively. The first step (step 900 in FIG. 9) in the exemplary process is to provide a semiconductor substrate 11. Substrate 11 may have a thickness of, for example 700 μm and a resistivity of 5 mΩ-cm (for an N+ doping for example). Next, at step 902, a first n-type portion 12 of the transistor drain region is formed over substrate 11, to a thickness determined by a thermal oxide layer thickness (e.g. 1.5 μm) that is to be grown from epitaxial layer 12 later in the process and a thickness required to create the transistor cell and an n− drain region beneath the cell. From this first portion 12 of the drain region, a thermal oxide layer 14 is formed at step 904. A cross-section of the structure formed, following completion of step 904, is shown in FIG. 10A.

After oxide layer 14 is formed, in step 906 oxide layer 14 is patterned using, for example, a photolithographic process as is known in the art, and etched, preferably anisotropically, to create oxide pillars 16. A cross-section of the structure, following completion of step 906, is shown in FIG. 10B. Next, at optional step 908, a short sacrificial oxidation, having a thickness of, for example, 0.03 μm, is formed over the exposed areas of epitaxial layer 12. Then, the sacrificial oxide is wet etched back to the epitaxial layer surface and the resulting structure is annealed in hydrogen to prepare the surface for the next step.

At step 910, a selective epitaxial growth (SEG) process is used to form an n-type remaining portion 18 of the transistor drain region. The structure following step 910 is shown in FIG. 10C. After the desired thickness of the remaining portion 18 of the drain region is obtained, at step 912 the doping source is switched to a p-type dopant (e.g. boron) and a p-body region 20 is formed using SEG. The structure following step 912 is shown in FIG. 10D. Optionally, an additional intrinsic SEG layer (not shown in the figures) can be grown, to compensate for up-diffusion from lower layers if necessary. Also, because only the doping source needs to be changed from step 910 to 912, both the remaining portion 18 of the drain region and p-body region 20 can be grown in situ.

Next, at step 914 the doping type is switched to n-type and an n+ source region 22 is grown over p− body region 20, again using SEG, to a thickness that meets the surface of the oxide pillars 16. The structure following step 914 is shown in FIG. 10E. At step 916, oxide pillars 16 are etched using an oxide biased etch that is preferably, anisotropic. The etch forms trenches 24 having a depth determined by the amount of oxide left at the bottom of the trenches 24, which is determined by the required gate-to-drain capacitance specification required for a particular application. The structure following step 916 is shown in FIG. 10F.

Following formation of trenches 24, an optional sacrificial oxide etch and anneal step 918 can be performed to prepare sidewalls of trenches 24 for gate oxidation.

The thickness of the sacrificial oxide is, for example, 0.02 μm. After the sacrificial oxide is wet etched back, the structure is annealed in hydrogen for approximately 3 minutes at a temperature of about 1060° C., followed by an argon anneal for approximately 20 minutes at a temperature of about 1100° C. At step 920, a gate oxide 26 is formed on the sidewalls of trenches 24 to a thickness of, for example, 0.04 μm. The structure following step 920 is shown in FIG. 10G.

After gate oxide 26 is formed, at step 922 trenches 24 are filled with polysilicon 28 to form a gate for the transistor. The thickness of polysilicon layer 28 is determined by the amount needed to fill trenches 24 without leaving a void. Polysilicon layer 28 is then doped by an implant process or by a diffusion process such as, for example, a POCL process.

At step 924, the portion of polysilicon layer 28, which is outside of trenches 24, is then etched using a silicon bias etch, thereby leaving a surface gate oxide 30 over n+ source region 22. The structure following step 924 is shown in FIG. 10I.

Next, a local oxidation of silicon (LOCOS) process is used to form a dielectric isolation region 32. The LOCOS process is performed as follows. First, at step 926, a nitride layer 34 is formed over surface gate oxide layer 30, which is used as a pad oxide. Then, at step 928 the nitride layer 34 and surface gate oxide layer 30 are masked (FIG. 10J) and etched to create openings to polysilicon layer 28 and upper comers of n+ source region 22. The structure following step 928 is shown in FIG. 10K. At step 930, dielectric isolation region 32 is formed by oxidizing the exposed polysilicon 28 and exposed upper comers of n+ source region 22. The structure following step 930 is shown in FIG. 10L. The LOCOS process is completed at step 932, at which step nitride layer 34 and surface gate oxide layer 30 are removed.

At step 934, p+ heavy body region 36 is formed by, for example, a standard implant and drive technique. The structure following step 934 is shown in FIG. 10M. And, finally, at step 936 a metal layer 38 is deposited over the structure, resulting in the final trench DMOS structure shown in FIG. 10N.

Alternative to the method described above, a method of manufacturing a trench DMOS transistor manufacturing method described above, the present invention provides a method of manufacturing a trench DMOS transistor having self-aligned dielectric isolation caps. The method follows the same or similar steps 900 through 912 as described above and then follows with steps 1100 through 1124 as described below in relation to cross-sectional FIGS. 12A-12J.

After body layer 20 is formed (step 912 in FIG. 9), at step 1100 a first n+ source region 40 is formed using an SEG process. N+ source region 40 is overgrown to a thickness greater than required to form the source for the transistor. The thickness, in this exemplary embodiment, would be about 0.5 μm. The extra thickness of n+ source region 40 is used later in the process to grow a thermal oxide isolation region. The structure following step 1100 is shown in FIG. 12A. Next, at step 1102 oxide pillars 42 are etched using an oxide biased etch that is preferably, anisotropic. The etch forms trenches 44 having a depth determined by the amount of oxide left at the bottom of the trenches 44, which is determined by the required gate-to-drain capacitance specification required for a particular application. The structure following step 1102 is shown in FIG. 12B.

Following formation of trenches 44, an optional sacrificial oxide etch and anneal step 1104 can be performed to prepare sidewalls of trenches 44 for gate oxidation. The thickness of the sacrificial oxide is, for example, 0.02 μm. After the sacrificial oxide is wet etched back, the structure is annealed in hydrogen for approximately 3 minutes at a temperature of about 1060° C., followed by an argon anneal for approximately 20 minutes at a temperature of about 1100° C. At step 1104, a gate oxide 46 is formed on the sidewalls of trenches 44 to a thickness of, for example, 0.04 μm. The structure following step 1104 is shown in FIG. 12C.

After gate oxide 46 is formed, at step 1108 trenches 44 are filled with polysilicon 48 to form a gate for the transistor. The thickness of polysilicon layer 48 is determined by the amount needed to fill trenches 44 without leaving a void. Polysilicon layer 48 is then doped by an implant process or by a diffusion process such as, for example, a POCL process. The structure following step 1108 is shown in FIG. 12D.

Next, at step 1110 polysilicon layer 48 is etched back using a blanket silicon-bias etch to a surface gate oxide 50 at a region outside trenches 44 and is overetched within trenches 44 to a predetermined polysilicon recess relative to surface gate oxide layer 50. The structure following step 1110 is shown in FIG. 12E. Then, at step 1112 surface gate oxide 50 is etched back using a blanket oxide-bias etch, including an over-etch so that a predetermined trench gate oxide recess is realized. This step may not be needed depending on the differences in oxidation rates of the polysilicon layer 48 and n+ source region 40. The structure following step 1112 is shown in FIG. 12F.

At step 1114, a blanket thermal oxide layer 52 is grown from n+ source region 40 to a desired thickness of, for example, 0.35 μm, for the purpose of creating a gate dielectric isolation region. The difference in consumption rates of polysilicon layer 48 and n+ source region 40 is compensated by the polysilicon recess that was formed in step 1110. This compensation assists in maintaining planarity of the structure. The structure following step 1114 is shown in FIG. 12G. Thermal oxide layer 52 is then masked and etched, at step 1116, using for example, an oxide-biased anisotropic etch, to create gate dielectric isolation caps 54. The structure following step 1116 is shown in FIG. 12H.

Following formation of gate dielectric isolation caps 54, an optional sacrificial oxide etch and anneal step 1118 can be performed to prepare the first portion of n+ source region 40 for a second portion 56 of n+ source region. The thickness of the sacrificial oxide is, for example, 0.02 μm. After the sacrificial oxide is wet etched back, the structure is annealed in hydrogen for approximately 1 minute at a temperature of about 1060° C. Then, at step 1120, second portion 56 of n+ source region is formed over the first portion 40 of n+ source region using an SEG process. After this step, the first and/or second portions of the n+ source region can be implanted to obtain a higher source doping concentration than may be achievable using SEG in situ doping. The structure following step 1120 is shown in FIG. 12I.

At step 1122, p+ heavy body region 58 is formed by, for example, a standard implant and drive technique. And, finally, at step 1124 a metal layer 60 is deposited over the structure, resulting in the final trench DMOS structure shown in FIG. 12J.

In, summary, the present invention provides novel methods of creating a thermally grown oxide of any thickness at the bottom of a silicon trench for a trench DMOS transistor. Unlike prior art attempts, the oxide is grown prior to formation of the trench and a selective epitaxial growth (SEG) process is used to form an epitaxial layer around the oxide pillars. Trenches are then patterned and etched in alignment with the pillars such that the trenches terminate on the top of the oxide pillars. Or, alternatively, the pillars are etched using an oxide-bias etch to form the trenches, the depth of the trenches determined by the amount of oxide left at the bottom of the trench following the oxide-bias etch.

Although the invention has been described in terms of a preferred methods and structure, it will be obvious to those skilled in the art that many modifications and alterations may be made to the disclosed embodiments without departing from the invention. Hence, these modifications and alterations are intended to be considered as within the spirit and scope of the invention as defined by the appended claims. 

What is claimed is:
 1. A method of forming a trench structure, the method comprising the steps of: providing a semiconductor substrate having a major surface; forming a dielectric pillar on the substrate major surface, the dielectric pillar extending substantially perpendicularly from the major surface; selectively forming a semiconductor layer around the dielectric pillar; and removing a predetermined first portion of the dielectric pillar to create a trench in the substrate, the trench defined by sidewalls and a bottom, wherein a second portion of the dielectric pillar having a predetermined thickness is left at the bottom of the trench following the step of removing a predetermined first portion of the dielectric pillar.
 2. The method of claim 1, further comprising the step of forming an oxide layer on the sidewalls of the trench.
 3. The method of claim 2, wherein the thickness of the second portion of the dielectric pillar is greater than a thickness of the oxide layer formed on the sidewalls of the trench.
 4. The method of claim 1, wherein the semiconductor layer is formed using selective epitaxial growth.
 5. A method of manufacturing a trench field effect transistor, comprising the steps of: providing a semiconductor substrate having a major surface and a first conductivity type; forming a plurality of dielectric columns extending perpendicularly from the major surface of the substrate; selectively forming a first semiconductor layer having the first conductivity type over exposed areas of the major surface of the substrate and around the dielectric columns; selectively forming a second semiconductor layer having a second conductivity type, opposite to that of the first conductivity type, over the first semiconductor layer and around the dielectric columns; selectively forming a third semiconductor layer having the first conductivity type over the second semiconductor layer and around the semiconductor columns; removing a predetermined portion of each dielectric column to create a plurality of trenches extending through the third, second and a portion of the first semiconductor layer, each trench defined by a bottom and sidewalls, wherein a second portion of each dielectric column having a predetermined thickness is left at the bottom of each trench; and lining the sidewalk of the trenches with a gate oxide.
 6. The method of claim 5, wherein the step of lining the sidewalls of the trenches further comprises forming a pad oxide layer on a horizontal surface of the third semiconductor layer.
 7. The method of claim 6, further comprising the step of filling the gate-oxide-lined trenches with a conductive material to form a gate for the transistor.
 8. The method of claim 7, further comprising the step of forming a nitride mask over the pad oxide layer.
 9. The method of claim 8, further comprising the step of selectively removing a portion of each of the pad oxide and nitride layers in regions above each conductive-material-filled trench.
 10. The method of claim 9, further comprising the step of forming a dielectric cap over each conductive-material-filled trench.
 11. The method of claim 10, further comprising the step of forming a heavy body having the second conductivity type within the third semiconductor layer and partially within the second semiconductor layer, wherein a doping concentration of the heavy body is greater than a doping concentration of the second semiconductor layer.
 12. The method of claim 7, further comprising the step of etching back the conductive material to a predetermined recess within the trenches.
 13. The method of claim 12, further comprising the step of removing the pad oxide layer.
 14. The method of claim 13, further comprising the step of forming a blanket dielectric layer over the openings of the trenches and over the exposed portions of the third semiconductor layer.
 15. The method of claim 14, wherein the blanket dielectric layer is formed by way of thermal oxidation of exposed portions of conductive material and exposed portions of the third semiconductor layer.
 16. The method of claim 15, further comprising the step of removing a portion of the blanket dielectric layer to leave dielectric caps over the trenches, which extend partially into the third semiconductor layer.
 17. The method of claim 16, further comprising the step of selectively forming a fourth semiconductor layer having the first conductivity type over the third semiconductor layer and around the dielectric caps.
 18. The method of claim 17, further comprising the step of forming a heavy body having the second conductivity type within the third and fourth semiconductor layers and partially within the second semiconductor layer, wherein a doping concentration of the heavy body is greater than a doping concentration of the second semiconductor layer.
 19. The method of claim 17, wherein the step of forming a fourth semiconductor layer having the first conductivity type is controlled so that the resulting fourth semiconductor layer has an exposed surface that is substantially planar to exposed surfaces of the dielectric caps.
 20. The method of claim 19, wherein the dielectric caps have lateral dimensions within the plane of the exposed surface of the dielectric caps that are approximately equal to lateral dimensions of the trenches in the same plane.
 21. The method of claim 5, wherein the thickness of the second portion of the dielectric column is greater than a thickness of the oxide layer lining the sidewalls of the trenches. 